WSC291 »
High strength semi-conductive water blocking core screen for helical applications.
Black polyester non-woven laminate with reinforcement and super absorbent layers.
Thickness mm - 0.34
Weight g/m2 - 91
Longitudinal Tensile Strength N/cm - 50
Swell mm (1/10 minutes) - 6/7
|
|
|
WSC292 »
High strength semi-conductive water blocking core screen for helical applications.
Black polyester non-woven laminate with reinforcement and super absorbent layers.
Thickness (mm) - 0.35
Weight (g/m2) - 96
Longitudinal Tensile Strength (N/cm) - 50
Swell (mm) 1/10 minutes - 10/11
|
|
|
WSC293 »
High strength semi-conductive water blocking core screen for helical applications.
Black polyester non-woven laminate with reinforcement and super absorbent layers.
Thickness (mm) - 0.39
Weight (g/m2) - 110
Longitudinal Tensile Strength (N/cm) - 50
Swell (mm) 1/10 minutes - 14/15
|
|
|
WSC294 »
High strength semi-conductive water blocking core screen for helical applications.
Black polyester non-woven laminate with reinforcement and super absorbent layers.
Thickness (mm) - 0.40
Weight (g/m2) - 120
Longitudinal Tensile Strength (N/cm) - 50
Swell (mm) 1/10 minutes - 20/21
|
|
|
WSD291 »
High strength insulative water blocking for helical application.
White polyester non-woven laminate with reinforcement & super absorbent layer.
Thickness (mm) - 0.32
Weight (g/m2) - 72
Longitudinal Tensile Strength (N/cm) - 50
Swell (mm) 1/10 minutes - 6/7
|
|
|
WSD292 »
High strength insulative water blocking for helical application,
White polyester non-woven laminate with reinforcement & super absorbent layer.
Thickness (mm) - 0.36
Weight (g/m2) - 77
Longitudinal Tensile Strength (N/cm) - 50
Swell (mm) 1/10 minutes - 10/11
|
|
|
WSD293 »
High strength insulative water blocking for helical application.
White polyester non-woven laminate with reinforcement & super absorbent layer.
Thickness (mm) - 0.38
Weight (g/m2) - 88
Longitudinal Tensile Strength (N/cm) - 50
Swell (mm) 1/10 minutes - 14/15
|
|
|
WSD294 »
High strength insulative water blocking for helical application.
White polyester non-woven laminate with reinforcement & super absorbent layer.
Thickness (mm) - 0.40
Weight (g/m2) - 97
Longitudinal Tensile Strength (N/cm) - 50
Swell (mm) 1/10 minutes - 20/21
|
|
|
WSC241 »
High water blocking capacity.
Black polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.21
Weight (g/m2) - 76
Longitudinal Tensile Strength (N/cm) - 30
Swell (mm) 1/10 minutes - 5/7
|
|
|
WSC242 »
Semi-conductive high swell speed bedding/binder used in the core screen area of power cable.
Black semi-conductive polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.25
Weight (g/m2) - 95
Longitudinal Tensile Strength (N/cm) - 30
Swell (mm) 1/10 minutes - 10/11
|
|
|
WSC243 »
For use in power cables.
Black polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.28
Weight (g/m2) - 95
Longitudinal Tensile Strength (N/cm) - 30
Swell (mm) 1/10 minutes - 10/11
|
|
|
WSC244 »
Semi-conductive very high swell speed bedding/binder used in the core screen area of the power cable.
Black semi-conductive polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.30
Weight (g/m2) - 100
Longitudinal Tensile Strength (N/cm) - 30
Swell (mm) 1/10 minutes - 20/21
|
|
|
WSC255 »
Increased strength, semi-conductive, high swell speed bedding/binder used in the core screen area.
Black semi-conductive polyester nonwoven laminate with polyester scrim reinforcement and a super absorbent layer.
Thickness (mm) - 0.40
Weight (g/m2) - 120
Longitudinal Tensile Strength (N/cm) - 40
Swell (mm) 1/10 minutes - 21/22
|
|
|
WSD242 »
High swell insulative tape for use in the core screen area.
White polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.28
Weight (g/m2) - 65
Longitudinal Tensile Strength (N/cm) - 25
Swell (mm) 1/10 minutes - 10/11
|
|
|
WSD244 »
Very high swell speed binder.
White polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.30
Weight (g/m2) - 85
Longitudinal Tensile Strength (N/cm) - 25
Swell (mm) 1/10 minutes - 20/21
|
|
|
WSD251 »
Up to 4-pair copper cables and fibre optic cables.
White polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.25
Weight (g/m2) - 60
Longitudinal Tensile Strength (N/cm) - 25
Swell (mm) 1/10 minutes - 6/7
|
|
|
WSD252 »
High swell speed binder.
White polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.28
Weight (g/m2) - 65
Longitudinal Tensile Strength (N/cm) - 25
Swell (mm) 1/10 minutes - 10/11
|
|
|
WSD253 »
Communication and optical fibre cables.
White polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.28
Weight (g/m2) - 76
Longitudinal Tensile Strength (N/cm) - 25
Swell (mm) 1/10 minutes - 15/17
|
|
|
WSD282 »
Increased strength high swell speed binder.
White polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.36
Weight (g/m2) - 87
Longitudinal Tensile Strength (N/cm) - 40
Swell (mm) 1/10 minutes - 10/11
|
|
|
WSD284 »
Increased strength very high swell speed binder.
White polyester nonwoven laminate with super absorbent layer.
Thickness (mm) - 0.40
Weight (g/m2) - 110
Longitudinal Tensile Strength (N/cm) - 40
Swell (mm) 1/10 minutes - 20/21
|
|
|
WSL2250 »
Communication and optical fibre cables.
Polyester film laminated onto a water-swellable tape.
Thickness (mm) - 0.26
Weight (g/m2) - 65
Longitudinal Tensile Strength (N/cm) - 25
Swell (mm) 1/10 minutes - 3/5
|
|
|
WSL2252 »
High swelling speed.
Polyester film laminated onto a water-swellable tape.
Thickness (mm) - 0.25
Weight (g/m2) - 75
Longitudinal Tensile Strength (N/cm) - 25
Swell (mm) 1/10 minutes - 5/7
|
|
|
WSM102 »
Seawater swell binder for marine cable applications.
White polyester nonwoven laminate with seawater super absorbent.
Thickness (mm) - 0.33
Weight (g/m2) - 92
Longitudinal Tensile Strength (N/cm) - 25
Swell (mm) 1/10 minutes - 0.9/1.1
|
|